This product belongs to the methacrylate, heated acrylic resin immediately reacts into polymer thermosetting plastic and fill the gaps, increasing the weight, density, and an-corrosion property of the wood, makes it easy to be processed into a variety of fine wood products.
● Product characters: amber to light blue liquid (fluorescent).
● Shelf life: the original packaging shelf life 3 years.
● Packing: 20Kg / barrel.
● Risk, irritation: with a slight irritation on some human's skin, with eye irritation, so please wash your hands with soap after contacting this product. This product is not a dangerous chemical.
Usage method:
1. First, bake and dry the timber in the oven at a temperature above 100 degrees, to make the micropores dry.
2. Soak the timber in the infiltration solution and put an iron block on it, keeping the timber under the liquid level.
3. Vacuum infiltration time: we generally recommend continuous vacuum pumping 25 minutes, and then hold pressure 1 to 2 hours according to the actual situation, theoretically the longer the better.
4. Pressure infiltration: pressure 0.4Mpa after vacuum impregnation completed, keeping 10 to 100 minutes,according to the actual situation to set. (Some loose wood does not need pressuring)
5. Lift the timber out after the infiltration is completed, drip and wrap it with tin foil, and then place it into a preheated oven for heat curing with high temperature .
6 Over 90℃ curing:Because the air heat conduction is slow,the proposed oven temperature is constant temperature of 120 to 130 degrees, according to the thickness and volume of wood,in order to shorten the time.Generally it takes about 90 minutes if heated at 130 degrees. With the higher temperature, the shorter time it takes. When the temperature is low, the time will be long.